Descriptions
No additives inside, halogen-free and Phthalate-Free Film with excellent adhesive compatibility and printability
Product Size
| ITEM NO. | Thickness (um) | Width*Length (m) | Weight (kg) |
| XGT-L100-2PET | 100 | 1.55*1000 | 460 |
| XGT-L130-2PET | 130 | 1.55*810 | 410 |
| XGT-L150-2PET | 150 | 1.55*810 | 435 |
| XGT-L175-2PET | 175 | 1.55*750 | 435 |
| XGT-L200-2PET | 200 | 1.55*670 | 420 |
Typical Physical Properties
| Property | Value | Unit | Test method |
| Hardness | 90 | shore A | ASTM D2240 |
| Tensile strength |
>40
|
MPa | ASTM D412 |
| Elongation at break |
>400
|
% | ASTM D412 |
| Light transmission | 92 | % | ASTM D1003 |
| Gloss 60° | 82 | ASTM D1003 | |
| UV resistance | No change at 3000 hours | A11 |
| ITEM NO. | XGT-L100-2PET | ||||
| SPEC | PET film（50±2µm） TPU FILM（100±5%µm） PET film（75±2µm） |
||||
| / | |||||
| LOT NO. |
20210315003
|
GRADE
|
A
|
||
|
ITEM
|
UNIT
|
STANDRAD
|
VALUE
|
TEST METHOD
|
|
| Physical Properties | TPU film thickness | µm | 100±5% | 101 | ASTM D374 |
| UV b value | / | <0.4 | 0.30 | ASTM E313 | |
| Max Force | N | >150 | 185.59 | ASTM D412 | |
| Tensile strength | Mpa | >40 | 70.94 | ASTM D412 | |
| Elongation at break | % | >400 | 567.72 | ASTM D412 | |
| 100 modulus | Mpa | >5 | 9.19 | ASTM D412 | |
| 300 modulus | Mpa | >12 | 27.37 | ASTM D412 | |
| Release force (PET 50±2µm) | gf/inch | / | 8.71 | 180° Peeling | |
| Release force (PET 75±2µm) | gf/inch | / | 15.06 | ||
|
ITEM NO.
|
XGT-L130-2PET
|
||||
|
SPEC
|
PET film（50±2µm）
TPU FILM（130±5%µm） PET film（75±2µm） |
||||
|
|
/
|
||||
|
LOT NO.
|
20210316013
|
GRADE
|
A
|
||
|
|
ITEM
|
UNIT
|
STANDRAD
|
VALUE
|
TEST METHOD
|
|
Physical Properties
|
TPU film thickness
|
µm
|
130±5%
|
132
|
ASTM D374
|
|
UV b value
|
/
|
<0.4
|
0.33
|
ASTM E313
|
|
|
Max Force
|
N
|
>150
|
242.40
|
ASTM D412
|
|
|
Tensile strength
|
Mpa
|
>40
|
72.29
|
ASTM D412
|
|
|
Elongation at break
|
%
|
>400
|
584.06
|
ASTM D412
|
|
|
100 modulus
|
Mpa
|
>5
|
9.43
|
ASTM D412
|
|
|
300 modulus
|
Mpa
|
>12
|
27.60
|
ASTM D412
|
|
|
Release force
(PET 50±2µm) |
gf/inch
|
/
|
5.46
|
180° Peeling
|
|
|
Release force
(PET 75±2µm) |
gf/inch
|
/
|
14.20
|
||
|
ITEM NO.
|
XGT-L150-2PET
|
||||
|
SPEC
|
PET film（50±2µm）
TPU FILM（150±5%µm） PET film（75±2µm） |
||||
|
|
/
|
||||
|
LOT NO.
|
20210322058
|
GRADE
|
A
|
||
|
|
ITEM
|
UNIT
|
STANDRAD
|
VALUE
|
TEST METHOD
|
|
Physical Properties
|
TPU film thickness
|
µm
|
150±5%
|
152
|
ASTM D374
|
|
UV b value
|
/
|
<0.40
|
0.33
|
ASTM E313
|
|
|
Max Force
|
N
|
>150
|
268.81
|
ASTM D412
|
|
|
Tensile strength
|
Mpa
|
>40
|
68.71
|
ASTM D412
|
|
|
Elongation at break
|
%
|
>400
|
598.33
|
ASTM D412
|
|
|
100 modulus
|
Mpa
|
>5
|
7.55
|
ASTM D412
|
|
|
300 modulus
|
Mpa
|
>12
|
23.25
|
ASTM D412
|
|
|
Release force
(PET 50±2µm) |
gf/inch
|
/
|
6.50
|
180° Peeling
|
|
|
Release force
(PET 75±2µm) |
gf/inch
|
/
|
11.21
|
||
|
ITEM NO.
|
XGT-L175-2PET
|
||||
|
SPEC
|
PET film（50±2µm）
TPU FILM（175±5%µm） PET film（75±2µm） |
||||
|
|
/
|
||||
|
LOT NO.
|
20210321040
|
GRADE
|
A
|
||
|
|
ITEM
|
UNIT
|
STANDRAD
|
VALUE
|
TEST METHOD
|
|
Physical Properties
|
TPU film thickness
|
µm
|
175±5%
|
175
|
ASTM D374
|
|
UV b value
|
/
|
<0.40
|
0.37
|
ASTM E313
|
|
|
Max Force
|
N
|
>150
|
299.70
|
ASTM D412
|
|
|
Tensile strength
|
Mpa
|
>40
|
66.66
|
ASTM D412
|
|
|
Elongation at break
|
%
|
>400
|
577.79
|
ASTM D412
|
|
|
100 modulus
|
Mpa
|
>5
|
8.44
|
ASTM D412
|
|
|
300 modulus
|
Mpa
|
>12
|
24.99
|
ASTM D412
|
|
|
Release force
(PET 50±2µm) |
gf/inch
|
/
|
6.00
|
180° Peeling
|
|
|
Release force
(PET 75±2µm) |
gf/inch
|
/
|
18.85
|
||
|
ITEM NO.
|
XGT-L200-2PET
|
||||
|
SPEC
|
PET film（50±2µm）
TPU FILM（200±5%µm） PET film（75±2µm） |
||||
|
|
/
|
||||
|
LOT NO.
|
20210321040
|
GRADE
|
A
|
||
|
|
ITEM
|
UNIT
|
STANDRAD
|
VALUE
|
TEST METHOD
|
|
Physical Properties
|
TPU film thickness
|
µm
|
200±5%
|
200
|
ASTM D374
|
|
UV b value
|
/
|
<0.40
|
0.27
|
ASTM E313
|
|
|
Max Force
|
N
|
>150
|
259.8
|
ASTM D412
|
|
|
Tensile strength
|
Mpa
|
>40
|
51.1
|
ASTM D412
|
|
|
Elongation at break
|
%
|
>400
|
608.7
|
ASTM D412
|
|
|
100 modulus
|
Mpa
|
>5
|
7.7
|
ASTM D412
|
|
|
300 modulus
|
Mpa
|
>12
|
19.1
|
ASTM D412
|
|
|
Release force
(PET 50±2µm) |
gf/inch
|
/
|
5.6
|
180° Peeling
|
|
|
Release force
(PET 75±2µm) |
gf/inch
|
/
|
11.2
|
||